material : Ni97%,Mn3%
Sample : Free
Diameter : 0.01-6.0mm
Surface : Bright
State : Soft, 1/2H, Hard
Packing : Spool+Box
0.25mm, 0.38mm, DIN200 Spool, Nickel Manganese Alloys wire NiMn3 / Pure NIckel Ni201,Ni200
1.Description
Manganese compounds have been used by man for thousands of years. The ancient Egyptians and Romans used manganese compounds for dyeing in glass manufacture. In 1774 Johann Gottlieb Gahn succeeded in extracting pure manganese from brownstone. In the structure of the earth's crust manganese is the second most common heavy metal after iron.
Important manganese ore deposits are to be found in South Africa, Australia, India, China, Mexico, Ukraine and Russia amongst others.
"Manganese nodules" can also be found in the deep sea.
2.Properties
Code No. | Main Composition % | ||
Ni | Mn | Si | |
NiMn2 | Bal. | 1.5-2.5 | 0.3 |
NiMn3 | Bal. | 2.3-3.3 | 0.3 |
NiMn5 | Bal. | 4.6-5.4 | 0.5 |
Manganese is a grey-white, hard heavy metal. In the air it remains stable by the formation of an oxide film.
Code No. | Dia. mm | TS. N/mm2 | Elongation % |
NiMn2 | ≤6.0 | ≥350 | ≥20 |
NiMn3 | ≤6.0 | ≥350 | ≥20 |
NiMn5 | ≤6.0 | ≥350 | ≥20 |
3. Specification
diameter:0.01mm-6.0mm
4.Application
Due to its high affinity to sulphur and oxygen it is a vital element for the metal industry.
About 90 to 95% of the produced amount, preferably ferromanganese is used in the iron and steel industry
Nickel 201 is a low carbon variety compared with Nickel 200, possessing low annealed hardness and a very low work-hardening rate, desirable for cold forming operations. It is highly resistant to corrosion by neutral and alkaline salt solutions, fluorine and chlorine, but in oxidising salt solutions severe attack will occur.
The applications of pure nickel includes food and synthetic fiber processing equipment, electronic parts, aerospace and missile components, handling of sodium hydroxide above 300℃.
Chemical Composition
Alloy | Ni% | Mn% | Fe% | Si% | Cu% | C% | S% |
Nickel 201 | Min 99 | Max 0.35 | Max 0.4 | Max 0.35 | Max 0.25 | Max 0.02 | Max 0.01 |
Physical Data
Density | 8.9g/cm3 |
Specific Heat | 0.109(456 J/kg.℃) |
Electrical Resistivity | 0.085×10-6ohm.m |
Melting Point | 1435-1445℃ |
Thermal Conductivity | 79.3 W/m-K |
Mean Coeff Thermal Expansion | 13.1×10-6m/m.℃ |